Fire clay and high Alumina Bricks 2:

 

uality Al2O3 % Min. Fe2O3 % Max.
P.C.E. (O.C) Min.
APPARENT POROSITY (%) Max
CCS (Kg/cm2)Min.
RUL (Ta°C) Min.
Bulk Density (gm/cc)Min.
Plc (%) Max.
APPLICATIONS AREA
NA 80 80 1.8 37 20 600 1520 2.75 ±0.5 at 1500°C/2 hrs EAF Roof,Ladle lining & other high heat duty Special application.
NA 85 85 1.5 38 19 700 1550 2.80 ±0.5 at 1500 °C/2 hrs Special type of high temerature & high abrasion application.
NA 80 P 80 1.8 37 17 750 1500 2.80 ±0.8 at 1500 °C/2 hrs Phosphate bonded bricks for Reheating furnace bottom & other special alllication where abrasion is high.
NA 80 P 85 1.5 38 17 900 1530 2..85 ±0.8 at 1500 °C/2 hrs Phosphate bonded bricks for Aluminium melting & holding furnace & reheating furnace bottom .
NA 88 RFB
88 1.8 38 15 1000 1580 2.90 ±0.5 at 1500 °C/2 hrs An excellent material for fired reheating furnace bottom.
NA 50 S 50 2.0 34 21 400 1450 2.30 ±1.8 at 1500 °C/2 hrs Dense bricks for petroleum plant Fertlizer,Aluminium industry.
NA 55 S 55 2.0 35 22 450 1460 2.35 ±1.0 at 1500 °C/2 hrs Dense volume stable bricks for reheating furnace roof, petroleum plant.
NA Sill. 58 1.5 36 22 400 1520 2.35 ±0.5 at 1500 °C/2 hrs For Glass industry & Frit furnace application.
NA 60 S 60 2.0 36 22 450 1500 2.40 ±0.8 at 1500 °C/2 hrs For CS2 furnace, Sulphur Furnace, Alkali Resistant bricks for cement rotary klin
NA 62 D 62 1.5 36 16 600 1520 2.55 ±0.5 at 1500 °C/2 hrs Low Porosity dense bricks for blast furnace. Glass tank Furnace & Frit furnace
NA 70 S 70 3.0 36 23 500 1460 2.65 ±2.0 at 1500 °C/2 hrs For buring zone of cement rotary klin.
NA 70 L 70 2.5 36 23 500 1480 2.60 ±2.0 at 1500 °C/2 hrs For buring zone of cement rotary klin.
NA 70 Li 70 1.5 37 22 600 1520 2.55 ±0.5 at 1500 °C/2 hrs Lime klin & buring Zone of cement rotary klin